Weltrode WC 6150 AC-DC
Sizes :
2.5 x 300 mm
3.15 x 350 mm
4 x 350 mm
Availability : In Stock
High Tensile Strength Electrode For Joining All And Any Steel In Existence Including Unknown Steels.
- The Unique Coating And Special Alloy Core Wire Produces A Homogeneous, Porosity Free Machinable Weld Deposit.
- The High Tensile Strength Of Weltrode WC 6150 Increase In Use Due To Its Work Hardening Qualities Giving The Most Reliable Welds.
- Controlled Penetration Provides Optimum Strength And Gives Best Results On Any Steels. Controlled “Silion” Content Prevents Cracking.
- The Unique Composition Of Weltrode WC 6150 Neutralises The Harmful Effects Of Carbon Pickup Or Dilution In Weld Metal Thus Eliminating Sidebead Cracking And Underbead Cracking.
- Pass On Pass Welding Without Slag Removal Possible Without Slag Entrapment.
- The Controlled Arc Drive And Fluidity Of Weltrode WC 6150 Enables It To Perform Well In Dirty Contaminated And Oil Saturated Weld Zones Thus Eliminating The Need To Carry The Necessary Preweld Operations And Saving Downtime.
- High Corrosion And Heat Resistance.
- Shock And Impact Resistance Equivalent To Manganese Alloy Steels And Other Steels Designed For Impact Applications.
- Weld All Carbon And Alloy Steels-Low-Medium-High In All Positions, Under All Conditions, Including Dissimilar Combinations.
- Weld All Tools Steels, Manganese Steels And Speciality Steels In Thick To Thin Designs.
- Drag Or Touch Welding Technique May Be Used, Particularly In Fillets Without Slag Interference.
- Successful Welds On Hot And Cold Shears, Drill Shanks, Springs, Drill Shank Extensions, Tap Extraction, And Heat Treat Baskets.
TensileStrength
As Welded 110,000PSI
As Work Hardened 175,000PSI
Hardness Brinell 280
Elongation 26%
- Clean Surface. Bevel Heavy Sections To Be Joined. Adust Amperage. Within Recommended Range And Deposit Electrode, Maintaining A Short To Medium Arc Length.
- Tilt The Electrode 15 Degrees In The Direction Of Travel. Raise Amperage Slightly And Drag Weld Inclining The Electrode 45 Degrees In The Direction Of Travel For Rapid Filleting.
- Back-Whip Craters And Remove Slag Between Passes Wherever Possible. On High Tool Steels It Is Advisable To Preheat According To Base Metal To Obtain Best Results.
- Use Any Constant Current AC Transformer Or DC Generator/Rectifier Provided A Minimum Of 55 Volts Open Circuit.
- DC Reverse Polarity (Electrode+) Or AC.