Weltrode WC 6200 Gold AC-DC
AWS/ASME IIC A 5.4 E312-17
DIN 8556 E29.9 R 23
ISO 3581 E29.9 R 23
Sizes :
2.5 x 300 mm
3.15 x 350 mm
4 x 350 mm
Availability : In Stock
Premium High Tensile Electrode For Welding Dissimilar Steel Combinations With Unmatched Crack Resistance.
- One Versatile Electrode For Welding Dissimilar Steels Of Varying Compositions.
- High Resistance To Underbead Cracking ,Hot Cracking And Stress Corrosion Cracking.
- Unmatched Corrosion And Heat Resistance.
- Controlled Ferrite Content In AnAustenitic Mix Prevents Cracking.
- Superior Flux Chemistry Of Weltrode WC 6200 Gold Provides For A Total And Highly Effective Flushing Away Of Surface Contaminants Such As Oil, Grease, Rust Etc To Give Most Reliable Welds In These Conditions Welds From Weltrode WC 6200 Gold Ensures Practically Less Distortion Warpage And Stress.
- Superior Resistance To Shock And Impact.
For Joining And Building Up Of All Kinds Of Steels Including
- Medium- Carbon Steel, High-Carbon Steel, Heat-Resistant Steel, Spring Steel, Shock- Resistant Steel, Vanadium Moly Steel, Chrome Steel, Hardened Steel.
- Manganese Steel, T-1 Steel, Quick Speed Steel, Cast Steel, Sulfur Bearing Steel, All Stainless Steels, Tool Steels And All Unidentified Steels.
- Heat Treatment Baskets, GearTeeth, Chain Links, Drives And Sprockets, Crane Rails And Brooms Leaf Springs Are Few Of Applications.
TensileStrength
As Welded 130,000 PSI
As Work Hardened 195,000 PSI
Hardness Brinell 320
YieldStrength 91,000 PSI
Elongation 35%
- Clean Weld Area.The Area In Which Weld Is To Be Made Should Be Free Of Rust, Grease, Paint And Other Material Which Cause Weld Contamination.
- Bevel Heavy Sections To Be Joined. Pre Heat High Alloy And High Carbon Steels To That Required By Base Metal.
- Adjust Amperage Within Recommended Range And Deposit Electrode, Maintaining A Short To Medium Arc Length.
- Tilt The Electrode 15 Degrees In The Direction Of Travel. Raise Amperage Slightly And Drag Weld Inclining The Electrode 45 Degrees In The Direction Of Travel For Rapid Filleting.
- Back Whip Craters And Remove Slag Between Passes Where Ever Possible. Peening To Release Stresses In Beneficial.
- Use Any Constant Current AC Transformer Or DC Generator/Rectifier Providing A Minimum Of 55 Volts Open Circuit.
- DC Reverse Polarity (Electrode+) Or AC.