Felix 231 AC-DC
AWS/ASME A 5.4 E 312-17
DIN 8556 : E 29.9 R 23
ISO 3581 : E 29.9 R 32
Sizes :
2.5 x 300 mm
3.15 x 350 mm
4 x 350 mm
Customized Sizes Can Be Made.
Availability : In Stock
Highest Crack Resistant High Tensile Electrode For Joining All And Any Steels Including Dissimilar Steels.
- Special Flux Formulation Produces A Homogeneous, Porosity Free Machinable Weld Deposit.
- Tensile Strength Increases In Use Due To Its Work Hardening Qualities Giving The Most Reliable Welds.
- Excellent Spray Arc Transfer And Easy Slag Removal.
- High corrosion And Heat Resistance.
- Shock And Impact Resistance Equivalent To Manganese Alloy Steels And Other Steels Designed For Impact Applications.
- Weld All tool Steels, Manganese Steels And Speciality Steels In Thick To Thin Designs.
- Ideal For Joining Tool Steels, Spring Steels, Manganese Alloyed Steels, Rail Steels And Cast Steels.
- Weld All Carbon And Alloy Steels-Low-Medium-High In All Positions, Under All Conditions, Including Dissimilar Combinations.
Tensile Strength 122000 PSI
Tensile Strength As Work Hardened 186000 PSI
Yield Strength 90000 PSI
Elongation 30 %
Hardness 245 Brinell
- Clean Surface. Bevel Heavy Sections To Be Joined.
- Adjust Amperage Within Recommended Range And Deposit Electrode, Maintaining A Short To Medium Arc Length.
- Back-Whip Craters And Remove Slag Between Passes Where Ever Possible.
- On High Tool Steels It Is Advisable To Preheat According To Base Metal To Obtain Best Results.
- DC Reverse Polarity (Electrode +ve) Or AC.