Felix 222 DC (308L-15)
AWS /ASME A5.4 E 308L-15
ISO 3581 E 19.9 L B 22
Sizes :
2.5 x 300 mm
3.15 x 350 mm
4 x 350 mm
Customized Sizes Can Be Made.
Availability : In Stock
Premium Low Carbon High Crack Resistance Basic Electrode For Welding 18 Cr-8 Ni Austenitic Stainless Steels.
- Low Carbon Alloyed Wire In Felix 222 Eliminates Carbide Precipitation During Welding As Well As Weld Service.
- Weld Deposits Are Free Of Porosity With Good Resistance To Corrosion.
- Basic Coating Of Felix 222 Gives Highest Crack Resistance.
- Excellent Results On DC Reverse Polarity.
- Good Results On Heavy Sections Due To High Ductility.
- Basic Coated Electrode For Welding 301, 302, 303, 304L, 308, 308L, 321 Grade Stainless Steels.
- For Welding Stainless Steel Valves, Tanks, Pipes And Lining In Refineries, Oil And Gas, Food, Beverage, Nuclear, Pharmaceutical And Chemical Industries.
Tensile Strength 75000 PSI
Tensile Strength As Work Hardened 90000 PSI
Yield Strength 55000 PSI
Elongation 40 %
Inpact Energy (150-V/+20º C) Min 47 J
- Clean Weld Area. The Material To Be Welded Should Be Free Of Oil, Grease And Dust.
- Arc Length Should Be Kept As Short As Possible. Avoid Excessive Wide Weaving.
- Stringer Beads Are Recommended. If Necessary Redry Electrodes At 250° C For One Hour Before Use.
- DC Reverse Polarity (Electrode +Ve).