Weltrode 1460 AC-DC
AWS/ASME A 5.4 E 316L-16
DIN 8556: E 19.12.3 LR 26
ISO 3581: E 19.12.3 LR 32
Sizes :
2.0 x 300 mm
2.5 x 350 mm
3.2 x 350 mm
4.0 x 350 mm
Availability : In Stock
Premium Rutile Based Low Carbon Electrode for Welding Cr- Ni - Mo Stainless Steel .
- Excellent Resistance To Ptting, Acid and Corrosion .
- Low Carbon Content Reduces Susceptibilty to Intergranular Carbide Precipitation and Intergranular Corrosion .
- Good Results On Titanium and Niobium Stabilized Versions Of 316L Stainess Steels .
- Porosity Free Welds Due To Unique Moisture Resistant Formula .
- Excellent Arc Stability , Self peeling Slag , High Resistance to Porosity , Radiography Quality Weld .
- For Welding 316, 316L, 317, 317L And 318 Grade Stainless Steels .
- Industries - Chemicals , Food , Textile , Paint , Pharmaceuticals, Pulp And Paper .
| Tensile Strength | 87000 PSI | |||
| Yield Strength | 64000 PSI | |||
| Elongation | 42% | |||
- Clean Weld Area .
- The Material To Be Welded Should Be Free Of Oil , Grease And Dust .
- Arc Length Should Be kept As Short As Possible .
- Avoid Excessive Wide Weaving .
- Stringer Beads Are Recommended .
- Redry Electrodes At 200° C For One Hour Before Use .
- DC Reverse Polarity (Electrode +ve) Or AC .