Weltrode 1100 AC-DC
AWS /ASME A5.4 E 308L-16
BS 2926 -1984 19.9 LR
ISO 3581 E 19.9 L R 32
Sizes :
2.0 x 300 mm
2.5 x 350 mm
3.2 x 350 mm
4.0 x 350 mm
Availability : In Stock
Premium Low Carbon High Crack Resistance Electrode For Welding Austenitic Stainless Steels. Excellent For Welding 18 Cr-8 Ni Steels .
- Low Carbon Content In Weltrode 1100 AC-DC Eliminates Carbide Precipitation During Welding As Well As Weld Service .
- High Resistance To Weld Metal Porosity .
- High Corrosion Resistance In Oxidizing Environments .
- Crack Resistant As Deposits Have Ferrite Content In Range Of 5 - 10 % .
- Radiographic Quality, Easy Restrike, Smooth Bead Appearance And Self Peeling Slag .
- Rutile Coated Electrode For Welding 301 , 302 , 303 , 304L , 304LN , 308 , 308L , 321 , CF3 , CF8 Grade Stainless Steels .
-
For Welding Stainless Steel Valves ,Tanks , Pipes And Lining In Refineries , Oil And Gas , Food , Beverage , Nuclear , Pharmaceutical And Chemical Industries .
-
For Overlays Giving 308 Type Cmoposition .
| Tensile Strength | 80000 PSI | |||
| Tensile Strength As Work Hardened | 90000 PSI | |||
| Yield Strength | 58000 PSI | |||
| Elongation | 40% | |||
| Impact Energy (1SO-V ) | Min 40 J | |||
- Clean Weld Area . The Material To Be Welded Should Be Free Of Oil , Grease And Dust .
- Arc Length Should Be Kept As Short As Possible . Avoid Excessive Wide Weaving . Stringer Beads Are Recommended .
- DC Reverse Polarity (Electrode +Ve ) Or AC .
- If Necessary Redry Electrodes At 250° C For One Hour Before Use .