Weltrode WC 8350 AC-DC
Sizes :
2.5 x 300 mm
3.15 x 350 mm
4 x 350 mm
Availability : In Stock
Premium Electrode For Welding Cast Iron To Cast Iron To Steel With Maximum Machinability.
- Highly Balanced Nickel Content To Ensure Crack Resistance And Machinable Welds.
- The Problem Of High Carbon Weld Metal Deposits Is Avoided By Using Weltrode WC 8350 Which Produces Finely DividedGraphite No Porosity And A Readily Machinable Deposits.
- The Special Chemistry Of Weltrode WC 8350 Enables It To Weld Any Grade Of Cast Iron Present In The World Making It The Most Versatile Electrode.
- Smooth And Spatter Free Operation Providing High Quality Porosity Free Weld.
- The Tested Blend Of Elements In The Coating Of Weltrode WC 8350 Enables It To Weld In Contaminations.
- Welds Cast Iron To Steel.
- Pass On Pass Welding Without Slag Removal Possible.
- The Flux Coating Of Weltrode WC 8350 Does Not Contain “ Barium “ Thus Eliminating Hazardous Fumes During Welding.
- Perfect Color Match With The Base Metal.
- All Position Welding Possible.
- Weld All Grades Of Grey Cast Iron, Alloy Cast Iron Such As Mehanite, The Ductile Iron Including Nodular, Malleable And Spheroidal Graphitic Iron.
- Weld Furnace Grates, Burners, Sewer Pipe, Cast Iron Flanges And Fittings, Boilers, Stoves, And Other Components Subject To Temperature Rise In Service.
- Weld Iron Containing Nickel Or Copper And Also Those With Added Phosphorous.
TensileStrength 75,000 PSI
Hardness Brinell 180
YieldStrength 48,000 PSI
Elongation 20%
- Clean Surface If Possible. Otherwise Weld Through Contamination.
- Adjust Amperage Within Recommended Range And Deposit Electrode, Maintaining A Short To Medium Arc Length.
- Tilt The Electrode 30 Degrees In The Direction Of Travel. Use Stringer Bead Or Moderate Weave Technique And Back-Whip All Craters.
- Use DC Reverse (+).