Felix 257 AC-DC
AWS/ASME A5.4 E 316L-16
DIN 8556 : E 19.12.3 LR 26
ISO 3581: E 19.12.3 LR 32
Sizes :
2.5 x 300 mm
3.15 x 350 mm
4 x 350 mm
Customized Sizes Can Be Made.
Availability : In Stock
Premium Low Carbon Electrode for Welding Cr - Ni - Mo Stainless Steel.
- Excellent Resistance To Acid and Corrosion.
- Low Carbon Content Ensures High Resistance To Intercrystalline Corrosion.
- Good Results On Titanium and Niobium Stabilized Versions Of 316 L Stainess Steels.
- High Crack Resistance Due To Adequate Ferrite Content.
- Good Elimination of Carbide Precipitation Due to Welding.
- 316 And 316 L Stainless Steels.
- For Welding Tanks, Digestors Evaporators, Pipes, Equipment Made Of Cr- Ni- Mo Steels Or Cast Steels.
- Industries - Chemicals, Food, Textile, Paint, Pharmaceuticals Pulp And Paper.
Tensile Strength 80000 PSI
Tensile Strength As Work Hardened 97000 PSI
Yield Strength 56000 PSI
Elongation 42 %
Inpact Energy (150-V/+20° C ) Min 47 J
- Clean Weld Area. The Material To Be Welded Should Be Free Of Oil, Grease And Dust.
- Arc Length Should Be kept As Short As Possible. Avoid Excessive Wide Weaving.
- Stringer Beads Are Recommended. Redry Electrodes At 200° C For One Hour Before Use.
- DC Reverse Polarity (Electrode +ve) Or AC.